User:MSCI100SLL/sandbox

Composition
US patent 4,444,925 lists the components of Gyp-Crete® as atmospheric calcined gypsum, sand, water, and small amounts of various additives. Additives listed include polyvinyl alcohol, an extender such as sodium citrate or fly ash, a surfactant such as Colloid defoamer 1513 DD made by Colloids, Inc., and a fluidizer based on sodium or potassium derivatives of naphthalene sulfonate formaldehyde condensate. One example mix is shown below.

The purpose of the polyvinyl alcohol is to prevent the surface of the concrete from becoming dusty. While the exact mechanism is not known, it is thought that as the concrete sets, water migrates to the surface, bringing with it fine, dusty particles. When the water evaporates, the dusty particles are deposited on the surface. It is thought that the polyvinyl alcohol prevents the dusty particles from migrating upwards with the water.

The mix is prepared on site using a specialized truck. The truck contains a tank for water, a mixing tank, a holding tank, a pump, and a conveyor for the sand and calcined gypsum. A hopper for the sand and gypsum is mounted externally on the vehicle.

To prepare the mix, the sand and calcined gypsum are added to the hopper and mixed. Most of the required water is added to the mixing tank, then the sand and calcined gypsum are mixed in. Once all the sand and calcined gypsum have been mixed in, the rest of the water is added until the proper consistency is attained. Finally, the additives are mixed in and the whole batch of concrete is moved to the holding tank to be pumped out into the required area via long hoses. A small sample is taken from the batch and set aside so that the set-up time can be observed and adjustments can be made to the amount of additives so that the timing is correct.

Once the mix has been poured, little leveling, if any, is needed. The mix should be smoothed gently with a flat board, such as a 40” 1x4. This helps to concentrate the calcined gypsum at the surface.

Previous Formulations
US patent 4,075,374 lists the formulation as 10 parts pressure calcined gypsum, 38-48 parts sand, and 4-10 parts water. 0.03 to 0.1 parts of a latex emulsion, such as Dow Latex 460, were also added. To prevent foaming, a defoamer such as WEX was added to the latex at a concentration of 0.2%. It was stated that gypsum calcined at atmospheric pressure produced poor results due to it having flaky particles, and that gypsum calcined under a pressure of 15-17 psi produced better results because it had denser, crystalline particles.

Later it was found that this original formulation expanded too much and in some instances floors cracked. US patent 4,159,912 describes changes made so that the expansion was greatly reduced. In that formulation, 5-8% of Portland cement was added to reduce the expansion. The latex emulsion and antifoaming agent were no longer necessary as the concrete was strengthened by the Portland cement. It was found that atmospheric calcined gypsum could be used for the majority of the calcined  gypsum if it was ball milled to change the texture. The proportion of sand was also changed, so that it was in a 1:1.3 to 1:3 ratio with the calcined gypsum. This resulted in a runnier mix, but the set up time was not changed.

Advantages and disadvantages
A 7 man work crew can lay 4-6 times as much gypsum concrete in a work day as regular poured Portland cement. This is due to the ease of leveling the very runny gypsum concrete versus normal concrete. In addition, if the wooden subfloor is first coated in a film of latex, the adhesion between the subfloor and the concrete is much better than the adhesion obtained with “normal” concrete. A further benefit is that nails can be driven through the cement into the subfloor without it chipping.