User:SpinningMelt/sandbox/Melt Spinning

For the polymer fiber forming process, see Spinning (polymers). The metal (A) is melted by induction coils (I) and pushed by gas pressure (P), in a jet through a small orifice in the crucible (K) over the spinning drum (B) where it is rapidly cooled to form the ribbon of amorphous material (C) Melt spinning is a technique used for rapid cooling of liquids. A wheel is cooled internally, usually by water or liquid nitrogen, and rotated. A thin stream of liquid is then dripped onto the wheel and cooled, causing rapid solidification. This technique is used to develop materials that require extremely high cooling rates in order to form, such as metallic glasses. The cooling rates achievable by melt-spinning are on the order of 104–107 kelvins per second (K/s).

Chill block melt spinning (CBMS) is a rapid solidification process primarily used for the production of thin metal ribbons. This process has gained wide acceptance as a means of producing amorphous and nanocrystalline materials for several technological applications in electronics.

Originating with Robert Pond in a series of related patents from 1958–1961 (US Patent Nos. 2825108, 2910744, and 2976590), the current concept of the melt spinner was outlined by Pond and Maddin in 1969, though, at first, liquid was quenched on the inner surface of a drum. Liebermann and Graham further developed the process as a continuous casting technique by 1976, this time on the drum's outer surface. The process can continuously produce thin ribbons of material, with sheets several inches in width commercially available.