Dear sir,

We are interpreting Titanium Castings(Ti6Al4V) as per ASTM E1320, which is produced through Investment Casting route & hipped,.

We are assuming that chances of inclusions in the castings are remote (casting is produced through Investment casting route) ,hence all the indications are shrinkage & accordingly we are interpreting the casting radiographs.

We have seen one crack like indication but there is no mention of crack in ASTM E1320, should we assume that cracks are not possible in Titanium castings, further we wish to clarify that such a tight crack is difficult to pick up in RT. We are of the opinion that it is the shrinkage & the size is reduced due to hipping.

My problem is that castings are already fitted, hence it is not available with us.

We wish to know how to proceed further?

Regards

ashwani kumar